点击图片查看原图
重要参数： 密度:1.64 g/cm3 缺口冲击强度:160 拉伸强度:125 MPa 断裂伸长率:4 % 弯曲强度:125 MPa弯曲模量:9600 MPa 热变形温度:239 ℃
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.64 | ||
| 模具收缩率 | 3.2mm(0.126in) | ASTM D-955 | 0.5 | % | |
| 机械性能 | 弯曲强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 125 | MPa |
| 断裂伸长率 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 4 | % | |
| 弯曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 9600 | MPa | |
| 弯曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 9600 | MPa | |
| 弯曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 13900 | MPa | |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 11569 | MPa | |
| 拉伸强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 141 | MPa | |
| 断裂伸长率 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 3.3 | % | |
| 压缩模量 | ASTM D-695 | 4100 | MPa | ||
| 弯曲强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 125 | MPa | |
| IZOD冲击强度 | 3.2mm(0.126in) | ASTM D-256 | 160 | J/m | |
| 断裂伸长率 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 4 | % | |
| 拉伸模量 | 3.2mm | ASTM D-638 | 10500 | MPa | |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 11569 | MPa | |
| 压缩模量 | ASTM D-695 | 4100 | MPa | ||
| 弯曲强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 158 | MPa | |
| 弯曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 13900 | MPa | |
| 拉伸模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 10500 | MPa | |
| IZOD冲击强度 | 3.2mm(0.126in) | ASTM D-256 | 160 | J/m | |
| 弯曲强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 158 | MPa | |
| 拉伸强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 125 | MPa | |
| 电气性能 | 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.001 | |
| 损耗因数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 介电强度 | 0.8mm | ASTM D-149 | 49 | Kv/mm | |
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 介电常数 | 0.8mm(0.032in) | ASTM D-150 | 2.9 | ||
| 介电常数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 4 | ||
| 损耗因数 | 0.8mm(0.032in) | ASTM D-150 | 0.013 | ||
| 介电强度 | 3.2mm | ASTM D-149 | 26 | Kv/mm | |
| 介电常数 | 0.8mm | ASTM D-150 | 3.3 | ||
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 4.1 | ||
| 介电常数 | 3.2mm(0.125in) | ASTM D-150 | 3.6 | ||
| 介电强度 | 1.6mm | ASTM D-149 | 41 | Kv/mm | |
| 损耗因数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.001 | ||
| 介电常数 | 3.2mm(0.125in) | ASTM D-150 | 3.6 | ||
| 损耗因数 | 0.8mm(0.032in) | ASTM D-150 | 0.029 | ||
| 损耗因数 | 0.8mm(0.032in) | ASTM D-150 | 0.009 | ||
| 损耗因数 | 3.2mm(0.125in) | ASTM D-150 | 0.013 | ||
| 介电常数 | 0.8mm(0.032in) | ASTM D-150 | 3.3 | ||
| 表面电阻率 | ASTM D-257 | >1×1016 | Ohm | ||
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 4.1 | ||
| 体积电阻率 | ASTM D-257 | >1×1016 | Ohm-cm | ||
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.002 | ||
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.001 | ||
| 介电常数 | 3.2mm(0.125in) | ASTM D-150 | 3.2 | ||
| 介电常数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 3.9 | ||
| 损耗因数 | 3.2mm(0.125in) | ASTM D-150 | 0.028 | ||
| 加工性能 | 损耗因数 | 3.2mm(0.125in) | ASTM D-150 | 0.008 | |
| 热性能 | 热变形温度 | 1.80MPa | ASTM D-648 | 239 | ℃ |
| 玻璃化转变温度 | ASTM D-3418 | 120 | ℃ | ||
| 模压温度范围 | 30-95 | ℃ | |||
| 干燥温度 | 135 | ℃ | |||
| 熔点 | ASTM D-3418 | 335 | ℃ | ||
| 解链温度范围 | 350-360 | ℃ | |||
| 其它性能 | 工业含水量 | <0.01 | % | ||
| RTI,Electrical | 1.5mm | UL 746-B | 130 | ℃ | |
| RTI,Mechanical with Impact | 1.5mm | UL 746-B | 130 | ℃ | |
| RTI,Mechanical without Impact | 1.5mm | UL 746-B | 130 | ℃ |
|
本公司长期供应LCP（液晶高分子）工程塑料、但不仅限于以下产品：
供应LCP美国杜邦：阻燃V-0级7130、6130、6130L、7130L、1110、16105、17101、17235、E7008；
供应LCP日本宝理：35%增强E471i；30%增强阻燃剂E130i；
供应LCP日本宝理：阻燃级C130、A130；玻纤增强级A150；
供应LCP日本宝理：超高耐热级高温刚性C135（HDT340℃）；
供应LCP日本住友：E4008、E5008L、E6008、E6006L、E6807LHF、E4008MR、E6006MR；
供应LCP日本东丽：L204G35、L204G40；
供应LCP新加坡杜邦：V-0阻燃级7130、6130、6130L、E7008；
供应LCP美国阿莫科：G930、GN930；
供应LCP日本石油化学：MG-350BPRL/PRL、NC-301B、HM-402B、HM-302。
优点：1、流动性高；2、尺寸安定性佳；3、流动性极佳；4、耐溶剂性；
5、高机械强度；6、难燃性。
用途：1、速接器、线圈、开关、插座等；2、泵零件、阀零件等；
3、汽车燃料外围零件等；4、电子炉用容器等。