PC德国科思创拜耳9425
PC德国科思创拜耳9425脱模性能良好，
PC德国科思创拜耳9425粘度高，
PC德国科思创拜耳9425阻燃
|
Makrolon® 9415(Z)（聚碳酸酯-PC塑料）
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.27 g/cc
|
0.0459 lb/in³
|
|
|
Water Absorption吸水率
|
0.29 %
|
0.29 %
|
Saturation in water
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
0.12 %
|
0.12 %
|
Equilibrium at 50% RH
|
|
Water Absorption at Saturation饱和水吸收率
|
0.29 %
|
0.29 %
|
|
|
Linear Mold Shrinkage 线性收缩率
|
0.0030 - 0.0050 cm/cm
|
0.0030 - 0.0050 in/in
|
ASTM D955
|
|
Melt Flow熔体流动速率
|
6.0 g/10 min
@Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min
@Load 2.65 lb, Temperature 572 °F |
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness, Rockwell M罗氏硬度M
|
75
|
75
|
ASTM D785
|
|
Tensile Strength, Ultimate极限拉伸强度
|
69.0 MPa
|
10000 psi
|
ASTM D638
|
|
Tensile Strength, Yield屈服拉伸强度
|
80.0 MPa
|
11600 psi
|
ASTM D638
|
|
Elongation at Break断裂伸长率
|
10 %
|
10 %
|
ASTM D638
|
|
Elongation at Yield屈服伸长率
|
5.0 %
|
5.0 %
|
ASTM D638
|
|
Tensile Modulus拉伸模量
|
4.00 GPa
|
580 ksi
|
|
|
Flexural Yield Strength弯曲屈服强度
|
103 MPa
|
14900 psi
|
at 5% strain; AST
|