| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
--- |
ASTM D-1505 |
0.938 |
g/cm3 |
frame="void">
| 熔体流动速率 |
MI |
| HLMI |
|
frame="void">
| 190℃/2.16kg |
| 190℃/21.6kg |
|
frame="void">
| ASTM D-1238 |
| ASTM D-1238 |
|
|
frame="void">
| g/10min |
| g/10min |
|
| 机械性能 |
正切弯曲模量 |
--- |
ASTM D-790 |
760 |
MPa |
| 落锤冲击 |
66cm |
ASTM D-1709 |
165 |
g |
| 抗冲击强度(Spencer) |
--- |
ASTM D-3420 |
0.35 |
J |
frame="void">
| 屈服拉伸强度 |
MD |
| TD |
|
frame="void">
| 50mm/min |
| 50mm/min |
|
frame="void">
| ASTM D-882 |
| ASTM D-882 |
|
|
|
frame="void">
| 断裂伸长率 |
MD |
| TD |
|
frame="void">
| 50mm/min |
| 50mm/min |
|
frame="void">
| ASTM D-882 |
| ASTM D-882 |
|
|
|
frame="void">
| 埃尔门多夫撕裂强度 |
MD |
| TD |
|
--- |
frame="void">
| ASTM D-1922 |
| ASTM D-1922 |
|
|
|
| 热 性 能 |
脆化温度 |
--- |
ASTM D-746 |
<-75 |
℃ |